Gilson Gray Iron 9000 Capping Compound (1 to 39 Bags)

Gilson Gray Iron 9000 Capping Compound is a new and improved sulfur mortar capping compound that ensures even load distribution during concrete strength testing. Ultra-thin, low-odor flakes are carefully formulated from sulfur and mineral filler.

Gray Iron melts quickly at 230°–240°F (110°–115°C), with a wide optimum pouring range of 265°–290°F (129°–143°C). The set time is about one minute, and shrinkage is minimal.

If accidental overheating occurs, the compound remains usable after cooling, and solidified material can be re-melted with no loss of properties. Compressive strength exceeds 8,000psi at two hours for ASTM C617 tests of 2in cubes, and bond strength is 150psi or more. The strength and bond properties of capped specimens do not degrade over time, even when stored in humid conditions.

Each bag weighs 50lb (22.68kg); order 40 or more bags for the value price option.

Features:

• Reliable sulfur mortar capping compound offers faster melting times and lower optimum pour temperature
• Ultra-thin flakes melt quickly at 230°–240° F (110°–115°C) with reduced odor
• The compound is not damaged by overheating and can be re-melted with no loss of properties
• ASTM C617 compliant

Included Items:

• Gilson Gray Iron 9000 Capping Compound

Accessories:

• Vertical Cylinder Cappers are available in three options by concrete cylinder size, 6x12, 4x8, or 3x6inc

Related blogs:

• Concrete Cylinder Testing - From the Field to the Lab
• Compressive Strength Testing: Sulfur Capping or Neoprene Pads?